Semiconductor device and method for fabricating the same

ABSTRACT

The semiconductor device comprises gate electrodes  50  formed on a silicon substrate  32  with a gate insulation film  48  formed therebetween, source/drain diffused layers  66   n,    66   p  formed in the silicon substrate  32  on both sides of the gate electrodes  50,  a skirt-like insulation film  58  formed on a lower part of the side wall of the gate electrode  50  and on the side end of the gate insulation film  48,  and a sidewall insulation film  60  formed on the exposed part of the side wall of the gate electrode  50,  which is not covered with the skirt-like insulation film  58  and the side surface of the skirt-like insulation film  58.

CROSS-REFERENCE TO RELATED APPLICATIONS

This application is a divisional of application Ser. No. 11/066,222 filed Feb. 28, 2005, which is based upon and claims priority of Japanese Patent Application No. 2004-317703, filed on Nov. 1, 2004, the contents being incorporated herein by reference.

BACKGROUND OF THE INVENTION

The present invention relates to a semiconductor device and a method for fabricating the same, more specifically a semiconductor device including a sidewall insulation film formed on the side wall of a gate electrode and a method for fabricating the same.

As the integration and the speed of semiconductor devices are increased, the nanonization of device structures, as of MOS transistors, etc., is rapidly progressing. Especially gate electrodes are formed not only in nanonized sizes but also with a small gap with respect to adjacent gate electrodes.

The background arts of the present invention are disclosed in e.g., Japanese published unexamined patent application No. Hei 07-307465 (1995).

However, when the gap between adjacent gate electrodes is small, the gap is often filled with an insulation film forming the sidewall insulation film. This makes difficult the ion implantation for forming impurity diffused regions for forming source/drain diffused layers.

On the other hand, too thin sidewall insulation film to be formed makes the distance between the source diffused layer and the drain diffused layer too small, which deteriorates the characteristics of MOS transistors and furthermore makes the operation itself difficult.

SUMMARY OF THE INVENTION

An object of the present invention is to provide a semiconductor device which has a small gap between the adjacent gate electrodes for the purpose of high integration of the semiconductor device but permits the sidewall insulation film to be formed without failure while suppressing the deterioration of the characteristics, and a method for fabricating the same.

According to one aspect of the present invention, there is provided a semiconductor device comprising: a gate electrode formed over a semiconductor substrate with a gate insulation film formed therebetween; a source/drain diffused layer formed in the semiconductor substrate on both sides of the gate electrode; and a sidewall insulation film including a skirt-like first insulation film formed on a lower part of a side wall of the gate electrode, and a second insulation film formed on an exposed part of the side wall of the gate electrode, which is not covered by the first insulation film and on a side surface of the first insulation film.

According to another aspect of the present invention, there is provided a method for fabricating a semiconductor device comprising the steps of: forming a gate electrode over a semiconductor substrate with a gate insulation film formed therebetween; implanting a dopant impurity into the semiconductor substrate with the gate electrode as a mask to form a first impurity diffused region in the semiconductor substrate on both sides of the gate electrode; depositing a first insulation film over the semiconductor substrate and anisotropically etching the first insulation film to form the first insulation film on a side wall of the gate electrode; implanting a dopant impurity into the semiconductor substrate with the gate electrode and the first insulation film as a mask to form a second impurity diffused region in the semiconductor substrate on both sides of the gate electrode; partially removing the first insulation film, leaving the first insulation film at a lower part of the side wall of the gate electrode; and depositing a second insulation film over the semiconductor substrate and anisotropically etching the second insulation film to form the second insulation film on an exposed part of the side wall of the gate electrode, which is not covered by the first insulation film and on a side surface of the first insulation film.

According to the present invention, the offset sidewall insulation film formed on the side wall of a gate electrode is removed, left at a lower end part of the side wall of the gate electrode to thereby form the skirt-like insulation film covering the ends of the source/drain diffused layer nearer to the gate electrode, and the sidewall insulation film is formed on the exposed part of the side wall of the gate electrode, which is not covered by the skirt-like insulation film and on the side surface of the skirt-like insulation film, whereby even when the gap between the adjacent gate electrodes is small, the sidewall insulation film can be formed in a required film thickness without failure while the characteristics are kept from being deteriorated.

BRIEF DESCRIPTION OF THE DRAWINGS

FIGS. 1A-1D are sectional views of the semiconductor device according to the present invention in the steps of the method for fabricating the same, which explain the principle of the present invention.

FIGS. 2A-2B are graphs of relationships between the period of time of removing the offset sidewall insulation film and the transistor characteristics for an NMOS transistor.

FIGS. 3A-3B are graphs of relationships between the period of time of removing the offset sidewall insulation film and the transistor characteristics for a PMOS transistor.

FIG. 4 is a graph of relationships between the period of time of removing the offset sidewall insulation film and the overlap capacitance.

FIG. 5 is a sectional view of the skirt-like insulation film of the present invention.

FIG. 6 is a sectional view of the semiconductor device according to a first embodiment of the present invention, which illustrates a structure thereof.

FIG. 7 is an enlarged sectional view of the semiconductor device according to the first embodiment of the present invention, which illustrates the structure thereof.

FIGS. 8A-8B, 9A-9B, 10A-10B, 11A-11B, 12A-12B, 13A-13B, 14A-14B, 15A-15B, 16A-16B, 17A-17B, 18A-18B and 19A-19B are sectional views of the semiconductor device according to the first embodiment of the preset invention in the steps of the method for fabricating the same, which illustrate the method.

FIGS. 20A-20B are enlarged sectional views of the semiconductor device according to modifications of the first embodiment of the present invention, which illustrate structures thereof.

FIG. 21 is a sectional view of the semiconductor device according to a second embodiment of the present invention, which illustrates a structure thereof.

FIG. 22 is an enlarged sectional view of the semiconductor device according to the second embodiment of the present invention, which illustrates the structure thereof.

FIGS. 23A-23B are sectional views of the semiconductor device according to the second embodiment of the present invention in the steps of the method for fabricating the same, which illustrate the method.

FIGS. 24A-24B are enlarged sectional views of the semiconductor device according to modifications of the second embodiment of the present invention, which illustrate structures thereof.

DETAILED DESCRIPTION OF THE INVENTION

[Principle of the Present Invention]

Recently, for the purpose of improving the characteristics of a MOS transistor, an offset is provided in impurity diffused regions forming the source/drain diffused layer. In this case, a plurality of sidewall insulation films are formed on the side wall of the gate electrode, and after the respective sidewall insulation films have been formed, the impurity diffused regions are suitably formed by ion implantation by self-alignment with the gate electrode with the sidewall insulation film formed on.

However, when a plurality of the sidewall insulation films are simply formed, there is a risk that when a gap between the adjacent gate electrodes is small, the gap between the adjacent gate electrodes may be filled with the insulation film. Specifically, for example, the gate electrodes of an about 30 nm-width and an about 100 nm-height are formed with a 200 nm-pitch, and a gap between the side walls of the adjacent gate electrodes is 170 nm, the gap between the adjacent gate electrodes may be filled with the insulation film. When the gap between the adjacent gate electrodes is filled with the insulation film, it makes difficult the ion implantation for forming the impurity diffused regions.

On the other hand, when the film thickness of the sidewall insulation film is too small, the distance between the source diffused layer and the drain diffused layer is too small, which deteriorates the characteristics of the MOS transistor and furthermore makes the operation itself difficult.

The inventor of the present application made earnest studies and has obtained an idea that after impurity diffused regions have been formed by self-alignment with the sidewall insulation film, the sidewall insulation film is removed with a lower end part thereof being left, and the sidewall insulation film is again formed, whereby the sidewall insulation film of a required film thickness can be formed while the gap between the adjacent electrodes is kept from being filled with the insulation film.

The principle of the method for fabricating the semiconductor device according to the present invention will be explained with reference to FIGS. 1A-1D, 2A-2B, 3A-3B, 4 and 5.

FIGS. 1A-1D are sectional views of the semiconductor device in the steps of the method for fabricating the semiconductor device according to the present invention, which explain the principle of the present invention. The sectional views on the left side in FIGS. 1A to 1D are of an NMOS transistor in the steps of the method for fabricating the semiconductor device, and the sectional views on the right side in FIGS. 1A to 1D are of a PMOS transistor in the steps of the method for fabricating the semiconductor device.

First, an offset sidewall insulation film 16 of, e.g., a silicon oxide film is formed on the side wall of a gate electrode 14 formed on a silicon substrate 10 with a gate insulation film 12 formed therebetween.

Then, for the NMOS transistor, a dopant impurity is implanted into the silicon substrate 10 on both sides of the gate electrode 14 by, e.g., ion implantation with the gate electrode 14 and the offset sidewall insulation film 16 as the mask. Thus, shallow n type first impurity diffused regions 18 n forming the extension regions of the extension source/drain structure are formed.

For the PMOS transistor, a dopant impurity is implanted into the silicon substrate 10 on both sides of the gate electrode 14 by, e.g., ion implantation with the gate electrode 14 and the offset sidewall insulation film 16 as the mask. Thus, shallow p type first impurity diffused regions 18 p forming the extension regions of the extension source/drain structure are formed (see FIG. 1A).

Next, an offset sidewall insulation film 20 of, e.g., a silicon oxide film is further formed on the side wall of the gate electrode 12 with the offset sidewall insulation film 16 formed on.

Next, for the NMOS transistor, with the gate electrode 14 and the offset sidewall insulation films 16, 20 as the mask, a dopant impurity is implanted by, e.g., ion implantation into the silicon substrate 10 on both sides of the gate electrode 14 with the offset sidewall insulation films 16, 20 formed on. Thus, n type second impurity diffused regions 22 n which are deeper than the first impurity diffused regions 18 n are formed.

For the PMOS transistor, with the gate electrode 14 and the offset sidewall insulation films 16, 20 as the mask, a dopant impurity is implanted by, e.g., ion implantation into the silicon substrate 10 on both sides of the gate electrode 14 with the offset sidewall insulation films 16, 20 formed on. Thus, p type second impurity diffused regions 22 p which are deeper than the first impurity diffused regions 18 p are formed (see FIG. 1B).

Then, the offset sidewall insulation films 16, 20 are partially removed from the upper end of the gate electrode 14. Thus, a skirt-like insulation film 24 of the partially left offset sidewall insulation films 16, 20 is formed on a lower side part of the side wall of the gate electrode 14 and the side end of the gate insulation film 12 (see FIG. 1C).

Then, relationships between conditions for partially removing the offset sidewall insulation films 16, 20 by wet etching to form the skit-like insulation films 24 and transistor characteristics will be explained.

FIGS. 2A-2B are graphs for the NMOS transistor. FIG. 2A is a graph of measured relationships between the gate length L_(g) and the threshold voltage V_(th). FIG. 2B is a graph of measured relationships between the ON-state current I_(on) and the OFF-state current I_(off) of the transistor. The gate length L_(g) was measured with a scanning electron microscope. In the graphs of FIGS. 2A-2B, the reference case that the offset sidewalls insulation films 16, 20 were not removed, and the cases that the removing period of time by wet etching was 38N, 41N and 45N were plotted. The reference case is indicated by the ♦ marks, the case of the 38N removing period of time is indicated by the ▪ marks, the case of the 42N removing period of time is indicated by the Δ marks, and the case of the 45N removing period of time is indicated by the × marks. The removing period times 38N, 41N and 45N are relative periods of time, and as the figure is larger, the removing period of time is longer.

FIG. 3A-3B are graphs for the PMOS transistor. FIG. 2A is a graph of measured relationships between the gate length L_(g) and the threshold voltage V_(th). FIG. 2B is a graph of measured relationships between the ON-state current I_(on) and the OFF-state current I_(off) of the transistor. The gate length L_(g) was measured with a scanning electron microscope. In the graphs of FIGS. 2A and 2B as well as in the graphs of FIGS. 2A-2B, the reference case that the offset sidewall insulation films 16, 20 were not removed, and the cases that the removing period of time by wet etching was 38N, 41N and 45N were plotted. The reference case is indicated by the ♦ marks, the case of the 38N removing period of time is indicated by the ▪ marks, the case of the 42N removing period of time is indicated by the Δ marks, and the case of the 45N removing period of time is indicated by the × marks.

In the NMOS transistor, as seen in the graph of FIG. 2A, the relationship between the gate length L_(g) and the threshold voltage V_(th) varies depending on the period of time of etching the offset sidewall insulation films 16, 20.

Also in the NMOS transistor, as seen the graph of FIG. 2B, as the period of time of etching off the offset sidewall insulation films 16, 20 is longer, the ON-state current I_(on) is smaller for the same ON-state current I_(off).

On the other hand, as seen in the graphs of FIGS. 3A-3B, even when the etching period of time of etching off the offset sidewall insulation film 16, 20 varies, the electric characteristics, make no substantially change.

FIG. 4 is a graph of the overlap capacitances C_(ov) between the gate electrode 14 and the source/drain diffused layer of the NMOS transistor which were measured with different removing period of time of wet etching off the offset sidewall insulation films 16, 20 and were plotted with respect to the removing periods of time. In FIG. 4 as well as FIGS. 2A-2B and 3A-3B, the reference case that the offset sidewall insulation films 16, 20 were not removed is indicated by the ♦ marks, the case of the 38N removing period of time is indicated by the ▪ marks, the case of the 42N removing period of time is indicated by the Δ marks, and the case of the 45N removing period of time is indicated by the X marks.

As evident in FIG. 4, as the period of time of wet etching off the offset sidewall insulation films 16, 20 is longer, the overlap capacitance C_(ov) is smaller.

As described above, the electric characteristics of the NMOS transistor are much varied and deteriorated, depending on the period of time of wet etching off the sidewall insulation films 16, 20. This reflects the phenomena that the dopant impurity concentration in the surface part (the regions enclosed by the dotted-line ellipse in FIG. 1C) of the impurity diffused region forming the source/drain diffused layer of the NMOS transistor is decreased by the wet etching.

On the other hand, the inventor of the present application has confirmed that both in the NMOS transistor and the PMOS transistor, the resistance value of the source/drain diffused layer makes substantially no change even with changes of the period of time of removing the offset sidewall insulation films 16, 20.

Considering that the resistance value of the source/drain diffused layer does not substantially change, the changes and the deterioration of the electric characteristics of the NMOS transistor shown in FIGS. 2A-2B and 4 will be due to the decrease of the dopant impurity concentration by the wet etching especially at the ends of the first impurity diffused regions 18 n nearer to the gate electrode.

Accordingly, if the ends of the first impurity diffused regions 18 n nearer to the gate electrode 14 are protected during the wet etching, the changes and the deterioration of the electric characteristics of the NMOS transistor could be suppressed. Specifically, the offset sidewall insulation films 16, 20 are left, covering the ends of the first impurity diffused regions 18n nearer to the gate electrode 14, i.e., the skirt-like insulation film 24 is formed, covering the ends of the first impurity diffused regions 18n nearer to the gate electrode 14, whereby the changes and the deterioration of the electric characteristics of the NMOS transistor can be suppressed.

Then, in the present invention, conditions for partially removing the offset sidewall insulation films 16, 20 by wet etching are so set that, as illustrated in FIG. 5, the skirt-like insulation films 24 cover the ends of the first impurity diffused regions 18 n, 18 p nearer to the gate electrodes 14. Thus, the skirt-like insulation films 24 can be formed by partially removing the sidewall insulation films 16, 20 while the deterioration of the transistor characteristics due to the decrease of the dopant impurity by the wet etching is suppressed.

For suppressing the decrease of the ON-sate current I_(on) of the NMOS transistor, the removing period of time may be set at, e.g., 38N excluding 38N.

Furthermore, for suppressing the decrease of the overlap capacitance C_(ov) of the NMOS transistor, the removing period of time may be set at, e.g., around 20N (a removing period of time corresponding to the regions enclosed by the dash-dotted line in FIG. 4).

After the skirt-like insulation film 24 has been thus formed, a sidewall insulation film 26 of, e.g., silicon oxynitride film is formed on the exposed part of the side wall of the gate electrode 14, which is not covered by the skirt-like insulation film 24, and on the side surface of the skirt-like insulation film 24.

Here, in the present invention, the offset sidewall insulation films 16, 20 are partially removed from the upper parts, and only the skirt-like insulation film 24 is formed on the side wall of the gate electrode 14 at a lower side part. Accordingly, even when the gap between adjacent gate electrodes 14 is small, the sidewall insulation film can be surely formed in a required film thickness without the gap being filled with the insulation film.

Then, for the NMOS transistor, with the gate electrode 14 and the sidewall insulation film 26 as the mask, a dopant impurity is implanted by, e.g., ion implantation into the silicon substrate 10 on both sides of the gate electrode 14 with the sidewall insulation film 26 formed on the side wall. Thus, n type third impurity diffused regions 28 n which are deeper than the second impurity diffused regions 22 n are formed.

Thus, for the NMOS transistor, the source/drain diffused layers 30 n of the extension source/drain structure of the first impurity diffused region 18 n, the second impurity diffused region 22 n and the third impurity diffused region 28 n are formed.

Then, for the PMOS transistor, with the gate electrode 14 and the sidewall insulation film 26 as the mask, a dopant impurity is implanted by, e.g., ion implantation into the silicon substrate 10 on both sides of the gate electrode 14 with the sidewall insulation film 26 formed on the side wall. Thus, p type third impurity diffused regions 28 p which are deeper than the second impurity diffused regions 22 p are formed.

Thus, for the PMOS transistor, the source/drain diffused layers 30 p of the extension source/drain structure of the first impurity diffused region 18 p, the second impurity diffused region 22 p and the third impurity diffused region 28 p are formed (see FIG. 1D).

As described above, according to the present invention, the offset sidewall insulation films 16, 20 are partially removed from the upper ends to thereby form the skirt-like insulation films 24 on the lower side parts of the side walls of the gate electrodes 14 and the side end of the gate insulation films 12, covering the sides of the gate electrode 14 in the first impurity diffused regions 18 n, 18 p, and then the sidewall insulation film 26 is formed. Thus, even when the gap between the adjacent gate electrodes 14 is small, the sidewall insulation film 26 can be surely formed in a required film thickness without the gap between the adjacent gate electrodes being filled with the insulation film suppressing the deterioration of the transistor characteristics is prevented.

A First Embodiment

The semiconductor device and the method for fabricating the same according to a first embodiment of the present invention will be explained with reference to FIGS. 6, 7, 8A-8B, 9A-9B, 10A-10B, 11A-11B, 12A-12B, 13A-13B, 14A-14B, 15A-15B, 16A-16B, 17A-17B, 18A-18B and 19A-19B. FIG. 6 is a sectional view of the semiconductor device according to the present embodiment, which illustrates a structure thereof. FIG. 7 is an enlarged view of the semiconductor device according to the present embodiment, which illustrates the structure thereof. FIGS. 8A-8B, 9A-9B, 10A-10B, 11A-11B, 12A-12B, 13A-13B, 14A-14B, 15A-15B, 16A-16B, 17A-17B, 18A-18B and 19A-19B are sectional views of the semiconductor device according to the present embodiment in the steps of the method for fabricating the same, which illustrate the method.

First, the structure of the semiconductor device according to the present embodiment will be explained with reference to FIGS. 6 and 7.

As illustrated in FIG. 6, trenches 34 are formed in a silicon substrate 32. A silicon oxide film 36 is formed on the side surfaces and the bottom surfaces of the trenches 34. A device isolation film 36 is buried in the trenches 34 with the silicon oxide film 36 formed on the side surfaces and the bottom surfaces. The device isolation film 38 defines device regions 40 a, 40 b.

A P well 42 is formed in the silicon substrate 32 in the device region 40 a. An N well 44 is formed in the silicon substrate 32 in the device region 40 b.

An NMOS transistor 46 n is formed in the device region 40 a. A PMOS transistor 46 p is formed in the device region 40 b.

First, the NMOS transistor 46 n formed in the device region 40 a will be explained.

On the silicon substrate 32 in the device region 40 a, a gate electrode 50 of polysilicon film is formed with a gate insulation film 48 formed therebetween. A metal silicide film 52 a is formed on the gate electrode 50.

In the silicon substrate 32 on both sides of the gate electrode 50, shallow n type first impurity diffused regions 54 n forming the extension regions of the extension source/drain structure are formed. P type pocket regions 56 p are formed below the bottoms of the first impurity diffused regions 54 n, adjacent to the first impurity diffused regions 54 n.

A skirt-like insulation film 58 of silicon oxide film is formed on a lower side part of the side wall of the gate electrode 50 and the side end of the gate insulation film 48. The skirt-like insulation film 58 covers the ends of the first impurity diffused regions 54 n nearer to the gate electrode 50.

A sidewall insulation film 60 of silicon oxynitride film is formed on the exposed part of the side wall of the gate electrode 50, which is not covered with the skirt-like insulation film 58 and on the side surface of the skirt-like insulation film 58.

In the silicon substrate 32 on both sides of the gate electrode 50 with the sidewall insulation film 60 formed on, n type second impurity diffused regions 62 n which are deeper than the first impurity diffused regions 54 n, n type third impurity diffused regions 64 n which are deeper than the second impurity diffused regions 62 n are formed. The ends of the second impurity diffused regions 62 n nearer to the gate electrode 50 are extended up to below the sidewall insulation film 60. The ends of the third impurity diffused regions 64 n nearer to the gate electrode 50 are extended up to the end of the sidewall insulation film 60.

The first impurity diffused region 54 n, the second impurity diffused region 62 n and the third impurity diffused region 64 n form a source/drain diffused layer 66 n of the extension source/drain structure. The ends of the source/drain diffused layers 66 n nearer to the gate electrode 50, i.e., the ends of the first impurity diffused regions 54 n nearer to the gate electrode 50 are covered by the skirt-shaped insulation film 58 as described above.

On the source/drain diffused layers 66 n on both sides of the gate electrode 50 with the sidewall insulation film 60 formed on, metal silicide films 52 b are formed.

Thus, the NMOS transistor 46 n including the gate electrode 50 and the source/drain diffused layers 66 n is formed in the device region 40 a.

Next, the PMOS transistor 46 p formed in the device region 40 b will be explained.

On the silicon substrate 32 in the device region 40 b, a gate electrode 50 of polysilicon film is formed with the gate insulation film 48 of silicon oxide film formed therebetween. The metal silicide film 52 a is formed on the gate electrode 50.

In the silicon substrate 32 on both sides of the gate electrode 50, shallow n type first impurity diffused regions 54 p forming the extension regions of the extension source/drain structure are formed. N type pocket regions 56 n are formed below the bottom of the first impurity diffused regions 54 p, adjacent to the first impurity diffused regions 54 p.

The skirt-like insulation film 58 of silicon oxide film is formed on a lower part of the side wall of the gate electrode 50 and the side end of the gate insulation film 48. The skirt-like insulation film 58 covers the ends of the first impurity diffused regions 54 p nearer to the gate electrode 50.

The sidewall insulation film 60 of silicon oxynitride film is formed on the exposed part of the side wall of the gate electrode 50, which is not covered with the skirt-like insulation film 58 and the side surface of the skirt-like insulation film 58.

In the silicon substrate 32 on both sides of the gate electrode 50 with the sidewall insulation film 60 formed on, p type second impurity diffused regions 62 p which are deeper than the first impurity diffused regions 54 p, p type third impurity diffused regions 64 p which are deeper than the second impurity diffused regions 62 p are formed. The ends of the second impurity diffused regions 62 p nearer to the gate electrode 50 are extended up to below the sidewall insulation film 60. The ends of the third impurity diffused regions 64 p nearer to the gate electrode 50 are extended up to the end of the sidewall insulation film 60.

The first impurity diffused region 54 p, the second impurity diffused region 62 p and the third impurity diffused region 64 p form a source/drain diffused layer 66 p of the extension source/drain structure. The ends of the source/drain diffused layers 66 p nearer to the gate electrode 50, i.e., the ends of the first impurity diffused regions 54 p nearer to the gate electrode 50 are covered by the skirt-shaped insulation film 58 as described above.

On the source/drain diffused layers 66 n on both sides of the gate electrode 50 with the sidewall insulation film 60 formed, the metal silicide films 52 b are formed.

Thus, the PMOS transistor 46 p including the gate electrode 50 and the source/drain diffused layers 66 p is formed in the device region 40 b.

FIG. 7 is an enlarged sectional view of the gate electrode 50 and its periphery of the semiconductor device according to the present embodiment. In FIG. 7, the NMOS transistor 46 n is illustrated, and the metal silicide films 52 a, 52 b are omitted.

As illustrated, the skirt-like insulation film 58 is formed on a lower part of the side wall of the gate electrode 50 and the side end of the gate insulation film 48. The skirt-like insulation film 58 covers the ends of the first impurity diffused regions 54 n forming the source/drain diffused layer 66 n, which are nearer to the gate electrode 50. The side surface of the skirt-like insulation film 58 is, e.g., inwardly convex.

The skirt-like insulation film 58 formed on the gate electrode 50 of the PMOS transistor 46 p is the same as that of the NMOS transistor 46 n illustrated in FIG. 7.

As described above, the semiconductor device according to the present embodiment is characterized mainly in that on a lower part of the side wall of the gate electrode 50 and the side end of the gate insulation film 48, the skirt-like insulation film 58 covering the ends of the first impurity regions 54 n, 54 p forming the source/drain diffused layer 66 n, 66 p, which are nearer to the gate electrodes is formed.

As will be described later, the skirt-like insulation film 58 is formed by partially wet etching off the offset sidewall insulation films used as the mask in the ion implantation for forming the first impurity diffused regions 54 n, 54 p and the second impurity diffused regions 62 n, 62 p. Accordingly, even when the gap between the adjacent gate electrodes 50 is small, the sidewall insulation film 60 can be surely formed in a required film thickness without the gap between the adjacent gate electrodes being filled with the insulation film 60. Accordingly, the leak current between the gate electrodes 50 and the source/drain diffused layers 66 n, 66 p can be sufficiently suppressed.

Because of the skirt-like insulation film 58 formed, covering the ends of the first impurity diffused regions 54 n, 54 p nearer to the gate electrodes 50, the deterioration of the transistor characteristics by the wet etching for forming the skirt-like insulation film 58 can be suppressed.

Because of the silicon oxide film, whose dielectric constant is 3.9, formed on lower parts of the gate electrodes 50 and the side end of the gate insulation film 48 as the skirt-like insulation film 58, the use of an insulation film of a high dielectric constant, such as silicon nitride film, silicon oxynitride film or others, can decrease the fringe capacitance.

Next, the method for fabricating the semiconductor device according to the present embodiment will be explained with reference to FIGS. 8A-8B, 9A-9B, 10A-10B, 11A-11B, 12A-12B, 13A-13B, 14A-14B, 15A-15B, 16A-16B, 17A-17B, 18A-18B and 19A-19B.

First, a silicon oxide film 68 of, e.g., a 10 nm-thickness is formed on the silicon substrate 32 by, e.g., thermal oxidation.

Next, on the silicon oxide film 68, a silicon nitride film 70 of, e.g., a 100-150 nm-thickness is deposited by, e.g., CVD (Chemical Vapor Deposition).

Then, a photoresist film 72 for exposing the regions for the device isolation film 38 to be formed in and covering the other region is formed on the silicon nitride film 70 by photolithography.

Then, with the photoresist film 72 as the mask, the silicon nitride film 70 is etched. Thus, openings 74 are formed in the silicon nitride film 70.

Next, with the photoresist film 72 and the silicon nitride film 70 as the mask, the silicon oxide film 68 and the silicon substrate 32 are etched. Thus, trenches 34 of, e.g., a 500 nm-depth are formed in the silicon substrate 32 (see FIG. 8B).

After the trenches 34 have been formed, the photoresist film 72 used as the mask is removed.

Next, a silicon oxide film 36 of, e.g., a 10 nm-thickness is formed on the side surfaces and the bottom surfaces of the trenches 34 by, e.g., thermal oxidation (see FIG. 9A).

Next, a silicon oxide film 38 of, e.g., a 500 nm-thickness is deposited on the entire surface by, e.g., high density plasma CVD (see FIG. 9B).

Then, the silicon oxide film 38 is polished by, e.g., CMP (Chemical Mechanical Polishing) until the surface of the silicon nitride film is exposed to thereby remove the silicon oxide film 38 on the silicon nitride film 70 (see FIG. 10A). Thus, the silicon oxide film 38 is planarized, filling the trenches 34 and the openings 74 with the silicon oxide film 38. Thermal processing for densifying the silicon oxide film 38 may be performed after the silicon oxide film 38 has been planarized. The thermal processing is performed in, e.g., a nitrogen atmosphere and at the thermal processing temperature of, e.g., 1000° C.

Next, the silicon nitride film 70 is removed by wet etching using, e.g., hot phosphoric acid (see FIG. 10B).

Thus, the device isolation films 38 of the silicon oxide film buried in the trenches 34 is formed by STI (Shallow Trench Isolation), and the device regions 40 a, 40 b are defined by the device isolation films 38. To define the device regions 40 a, 40 b, various methods other than STI may be used.

Then, after a sacrifice oxide film 76 of silicon oxide film is formed on the surface of the silicon substrate 32 by, e.g., thermal oxidation, the P well 42 and the N well 44 are formed by, e.g., ion implantation in the silicon substrate 32 respectively in the device region 40 a and in the device region 40 b (see FIG. 11A).

Then, the sacrifice oxide film 76 is removed by wet etching using, e.g., a hydrofluoric acid-based chemical liquid.

Next, the gate insulation film 48 of a silicon oxide film of, e.g., a 2 nm-thickness is formed on the silicon substrate 32 by, e.g., thermal oxidation.

Next, a polysilicon film 50 of, e.g., a 100 nm-thickness is formed on the entire surface by, e.g., low-pressure CVD. The film deposition temperature is, e.g., about 600° C.

Then, a photoresist film 78 for patterning the polysilicon film 50 is formed on the polysilicon film 50 by photolithography (see FIG. 12A).

Then, with the photoresist film 78 as the mask, the polysilicion film 50 is dry etched to thereby form the gate electrode 50 of the polysilicon film. After the gate electrode 50 has been formed, the photoresist film 78 used as the mask is removed (see FIG. 12B).

Next, a silicon oxide film 80 of, e.g., a 10 nm-thickness is deposited on the entire surface by, e.g., CVD (see FIG. 13A).

Then, the silicon oxide film 80 is anisotropically etched by, e.g., RIE (Reactive Ion Etching). Thus, the offset sidewall insulation film 80 of the silicon oxide film is formed on the side wall of the gate electrode 50 (see FIG. 13B).

Next, a photoresist film 82 exposing the device region 40 a for the NMOS transistor 46 n to be formed in and covering the rest region is formed by photolithography.

Next, with the gate electrode 50, the offset sidewall insulation film 80 and the photoresist film 82 as the mask, arsenic ions (As⁺), for example, are implanted at, e.g., a 3 keV acceleration voltage and a 1.5×10¹⁵ cm⁻² dose. Thus, n type first impurity diffused regions 54 n forming the extension regions of the extension source/drain structure are formed.

Next, with the gate electrode 50, the offset sidewall insulation film 80 and the photoresist film 82 as the mask, boron ions (B⁺), for example, are implanted at, e.g., a 7 keV acceleration energy and a 4×10¹³ cm⁻² dose. Thus, the p type pocket regions 56 p are formed below the bottom surface of the first impurity diffused regions 54 n, adjacent to the first impurity diffused regions 54 n (see FIG. 14A). In place of boron ions, indium ions (In⁺) may be implanted.

After the first impurity diffused regions 54 n and the pocket regions 56 p have been formed, the photoresist film 82 used as the mask is removed.

Then, a photoresist film 84 exposing the device region 40 b for the PMOS transistor 46 p to be formed in and covering the rest region is formed by photolithography.

Next, with the gate electrode 50, the offset sidewall insulation film 80 and the photoresist film 84 as the mask, boron ions, for example, are implanted at, e.g., a 1 keV acceleration voltage and a 2×10¹⁵ cm⁻² dose. Thus, the shallow p type first impurity diffused regions 54 p forming the extension regions of the extension source/drain structure are formed. In place of boron ions, boron fluoride ions (BF₂₊) may be implanted.

Then, with the gate electrode 50, the offset sidewall insulation film 80 and the photoresist film 84 as the mask, arsenic ions, for example, are implanted at, e.g., a 50 keV acceleration voltage and a 2×10¹³ cm⁻² dose. Thus, the n type pocket regions 56 n are formed below the bottom surface of the first impurity diffused regions 54 p, adjacent to the first impurity diffused regions 54 p (see FIG. 14B). In place of arsenic ions, antimony ions (Sb⁺) may be implanted.

After the first impurity diffused regions 54 p and the pocket regions 56 n have been formed, the photoresist film 84 used as the mask is removed.

Next, a silicon oxide film 86 of, e.g., a 20-40 nm-thickness is deposited on the entire surface by, e.g., CVD (see FIG. 15A).

Next, the silicon oxide film 86 is anisotropically etched by, e.g., RIE. Thus, the offset sidewall insulation film 86 of the silicon oxide film is further formed on the side wall of the gate electrode 50 with the offset sidewall insulation film 80 formed on (see FIG. 15B).

Next, a photoresist film 88 exposing the device region 40 a for the NMOS transistor 46 n to be formed in and covering the rest region is formed by photolithography.

Next, with the gate electrode 50, the offset sidewall insulation films 80, 86 and the photoresist film 88 as the mask, arsenic ions, for example, are implanted at, e.g., a 10 keV acceleration voltage and a 2×10¹⁵ cm⁻² dose. Thus, the n type second impurity diffused regions 62 n which are deeper than the first impurity region 54 n is formed (see FIG. 16A). In place of arsenic ions, phosphorus ions may be implanted.

After the second impurity diffused regions 62 n have been formed, the photoresist film 88 used as the mask is removed.

Next, a photoresist film 90 exposing the device region 40 b for the device region 40 b to be formed in and covering the rest region is formed by photolithography.

Then, with the gate electrode 50, the offset sidewall insulation film 80, 86 and the photoresist film 90 as the mask, boron ions, for example, are implanted at, e.g., a 1 keV acceleration voltage and a 2×10¹⁵ cm⁻² dose. Thus, the p type second impurity diffused regions 62 p which are deeper than the first impurity diffused regions 54 p are formed (see FIG. 16B). In place of boron ions, boron fluoride ions may be implanted.

After the second impurity diffused regions 62 p have been formed, the photoresist film 90 used as the mask is removed.

Next, by wet etching using, e.g., a hydrofluoric acid-based chemical liquid, the offset sidewall insulation films 80, 88 are removed, left at a lower part of the side wall of the gate electrode 50 and at the side end of the gate insulation film 48. Thus, the skirt-like insulation film 58 of silicon oxide film covering the ends of the first impurity diffused regions 54 n, 54 p nearer to the gate electrodes is formed (see FIG. 17A).

After the skirt-like insulation film 58 has been formed, ion implantation for compensating the dopant impurity in the surface of the silicon substrate 32 which has been decreased by the wet etching for forming the skirt-like insulation film 58 may be performed. In this case, a photoresist film (not illustrated) exposing the device region 40 a and covering the rest region is formed by photolithography, and then with the photoresist film and the gate electrode 50 as the mask, arsenic ions, for example, are implanted. After the ion implantation, the photoresist film used as the mask is removed. In the same way, a photoresist film (not illustrated) exposing the device region 40 b and covering the rest region is formed by photolithography, and then with the photoresist film and the gate electrode 50 as the mask, boron ions, for example, are implanted. After the ion implantation, the photoresist film used as the mask is removed.

Next, a silicon oxynitride film 60 of, e.g., a 80-100 nm-thickness is deposited on the entire surface by, e.g., CVD (see FIG. 17B).

Then, the silicon oxynitride film 60 is anisotropically etched by, e.g., RIE. Thus, the sidewall insulation film 60 of the silicon oxynitride film is formed on the exposed part of the side wall of the gate electrode, which is not covered by the skirt-like insulation film 58 and on the side surface of the skirt-like insulation film 58 (see FIG. 18A).

Here, the offset sidewall insulation films 80, 86 are partially removed from the upper ends thereof, and only the skirt-like insulation film 58 is formed on a lower part of the side wall of the gate electrode 50. Accordingly, even when the gap between the adjacent gate electrodes 50 is small, the sidewall insulation film 60 can be formed without the gap between the adjacent gate electrodes 50 being filled with the silicon oxynitride film.

Next, a photoresist film 92 exposing the device region 40 a for the NMOS transistor 46 n to be formed in and covering the rest region is formed by photolithography.

Then, with the gate electrode 50, the sidewall insulation film 60 and the photoresist film 92 as the mask, phosphorus ions, for example, are implanted at an 8 keV acceleration voltage and a 1×10¹⁶ cm⁻² dose. Thus, the n type third impurity diffused regions 64 n which are deeper than the second impurity diffused regions 62 n are formed (see FIG. 18B). In place of phosphorus ions, arsenic ions may be implanted.

After the third impurity diffused regions 64 n have been formed, the photoresist film 92 used as the mask is removed.

Next, a photoresist film 94 exposing the device region 40 b for the PMOS transistor 46 p to be formed in and covering the rest region is formed by, e.g., photolithography.

Next, with the gate electrode 50, the sidewall insulation film 60 and the photoresist film 94 as the mask, boron ions, for example, are implanted at, e.g., a 4 keV acceleration voltage and a 5×10¹⁵ cm⁻² dose. Thus, the p type third impurity diffused regions 64 p which are deeper than the second impurity diffused regions 62 p is formed (see FIG. 19A). In place of boron ions, boron fluoride ions may be implanted.

After the third impurity diffused regions 64 p have been formed, the photoresist film 94 used as the mask is removed.

Next, the implant dopant impurity is activated by thermal processing of, e.g., 1000° C. and 10 seconds. Thus, in the device region 40 a, the source/drain diffused layers 66 n of the extension source/drain structure formed of the first impurity diffused region 54 n, the second impurity diffused region 62 n and the third impurity diffused region 64 n are formed, and in the device region 40 b, the source/drain diffused layers 66 p of the extension source/drain structure formed of first impurity diffused region 54 p, the second impurity diffused region 62 p and the third impurity diffused region 66 p are formed.

Next, on the gate electrodes 50 and the source/drain diffused layers 66 n, 66 p, a metal silicide films 52 a, 52 b of a cobalt silicide film of, e.g., a 15 nm-thickness by salicide process (see FIG. 19B). The cobalt silicide film is selectively formed, e.g., by forming a cobalt silicide film by depositing a 5 nm-thickness cobalt film on the entire surface by sputtering, selectively reacting the cobalt film and the exposed parts of the silicon with each other and then removing the cobalt film which has not reacted. In place of cobalt silicide film, a nickel silicide film may be formed as the metal silicide films 52 a, 52 b.

Thus, the semiconductor device according to the present embodiment is fabricated.

As described above, according to the present embodiment, the offset sidewall insulation films 80, 86 are removed, left at a lower part of the side wall of the gate electrodes 50 and the side end of the gate insulation film 48 to thereby form the skirt-like insulation film 58 covering the ends of the first impurity diffused regions 54 n, 54 p nearer to the gate electrodes 50, and the sidewall insulation film 60 is formed on the exposed parts of the side walls of the gate electrodes 50 and the side surfaces of the skirt-like insulation film 58, whereby when the gap between the adjacent gate electrodes 50 is small, the sidewall insulation film 60 can be formed in a required film thickness without failure while the deterioration of the characteristics is suppressed.

(Modifications)

In the present embodiment, as illustrated in FIG. 7, the side surface of the skirt-like insulation film 58 is inwardly convex. However, the side surface of the skirt-like insulation film 58 is not limited to the configuration illustrated in FIG. 7. FIGS. 20A and 20B are enlarged sectional views of the semiconductor device according to modifications of the present embodiment, which illustrate structures thereof.

For example, as illustrated in FIG. 20A, the side surface of the skirt-like insulation film 58 may be outwardly convex.

As illustrated in FIG. 20B, the side surface of the skirt-like insulation film 58 may be substantially plane.

In FIGS. 20A and 20B, structures of the NMOS transistors 46n are illustrated, but configurations of the side surface of the skirt-like insulation film 58 of the PMOS transistor 46 p can be the same as illustrated in FIGS. 20A and 20B.

A Second Embodiment

The semiconductor device and the method for fabricating the same according to a second embodiment of the present invention will be explained with reference to FIGS. 21, 22 and 23A-23B. FIG. 21 is a sectional view of the semiconductor device according to the present embodiment, which illustrates a structure thereof. FIG. 22 is an enlarged sectional view of the semiconductor device according to the present embodiment, which illustrates the structure thereof. FIGS. 23A-23B are sectional views of the semiconductor device according to the present embodiment in the steps of the method for fabricating the same, which illustrate the method. The same members of the present embodiment as those of the semiconductor device and the method for fabricating the same according to the first embodiment are represented by the same reference numbers not to repeat or to simplify their explanation.

The structure of the semiconductor device according to the present embodiment is substantially the same as that of the semiconductor device according to the first embodiment. The semiconductor device according to the present embodiment is different from the semiconductor device according to the first embodiment in that in the former, the sidewall insulation film 60 formed on the exposed parts of the side walls of the gate electrodes 50 and the side surface of the skirt-like insulation film 58 is formed of the layer film of a silicon oxide film 96 and a silicon nitride film 98 sequentially laid the latter on the former.

As illustrated in FIG. 21, as in the semiconductor device according to the first embodiment, a skirt-like insulation film 58 of silicon oxide film is formed on lower end parts of the side walls of the gate electrodes 50 and the side end of a gate insulation film 48. The skirt-like insulation film 96 covers the ends of the first impurity diffused regions 54 n, 54 p nearer to the gate electrodes 50.

A silicon oxide film 96 is formed on the exposed parts of the side walls of the gate electrodes 50, which are not covered by the skirt-like insulation film 58 and the side surfaces of the skirt-like insulation film 58.

A silicon nitride film 98 is formed on the silicon oxide film 96.

Thus, the sidewall insulation film 60 is formed of the layer film of the silicon oxide film 96 and the silicon nitride film 98 thus sequentially laid the latter on the former.

FIG. 22 is an enlarged sectional view of the gate electrode 50 and its periphery of the semiconductor device according to the present embodiment. In FIG. 22, an NMOS transistor 46 n is illustrated, and metal silicide films 52 a, 52 b are omitted.

As illustrated, as in the semiconductor device according to the first embodiment, the skirt-like insulation film 58 is formed on a lower part of the side wall of the gate electrode 50 and on the side end of the gate insulation film 48. The skirt-like insulation film 58 covers the ends of the first impurity diffused regions 54 n forming the source/drain diffused layer 66 n, which are nearer to the gate electrode 50. The side surface of the skirt-like insulation film 58 is, e.g., inwardly convex.

The interface between the silicon oxide film 96 and the silicon nitride film 98 formed on the skirt-like insulation film 58 is inwardly convex, reflecting the configuration of the side surface of the skirt-like insulation film 58.

The skirt-like insulation film 58 formed on the gate electrode 50 of a PMOS transistor 46 p is the same as that formed on the gate electrode 50 of the NMOS transistor 46 n.

As described above, the sidewall insulation film 60 formed on the exposed parts of the side walls of the gate electrodes 50, which are not covered by the skirt-like insulation film 58 and the side surfaces of the skirt-like insulation film 58 may be formed of the layer of a plurality of insulation films.

Next, the method for fabricating the semiconductor device according to the present embodiment will be explained with reference to FIGS. 23A-23B.

First, the steps up to the step of forming the skirt-like insulation film 58 including the skirt-like insulation film 58 forming step are the same as the steps of the method for fabricating the semiconductor device according to the first embodiment illustrated in FIGS. 8A to 17A, and their explanation will be omitted.

Next, a silicon oxide film 96 of, e.g., a 10 nm-thickness is deposited on the entire surface by, e.g., CVD.

Next, a silicon nitride film 98 of, e.g., a 70 nm-thickness is deposited on the entire surface by, e.g., CVD (see FIG. 23A).

Next, the silicon nitride film 98 and the silicon oxide film 96 are anisotropically etched respectively by, e.g., RIE. Thus, the sidewall insulation film 60 of the layer of the silicon oxide film 96 and the silicon nitride film 98 sequentially laid the latter on the former is formed on the exposed parts of the side walls of the gate electrodes 50, which are not covered by the skirt-like insulation film 58 and on the side surfaces of the skirt-like insulation film 58 (see FIG. 23B).

The steps following the step of forming the third impurity diffused regions 62 n, 62 p are the same as those of the method for fabricating the semiconductor device according to the first embodiment illustrated in FIGS. 18B to 19B, and their explanation will be omitted.

As described above, according to the present embodiment, the offset sidewall insulation films 80, 86 are removed, left at lower parts of the side walls of the gate electrodes 50 and the side end of the gate insulation film 48 to thereby form the skirt-like insulation film 58 covering the ends of the first impurity diffused regions 54 n, 54 p, which are nearer to the gate electrodes 50, and the sidewall insulation film 60 is formed on the exposed parts of the side walls of the gate electrodes 50 and the side surfaces of the skirt-like insulation film 58, whereby when the gap between the adjacent gate electrodes 50 is small, the sidewall insulation film 60 can be formed in a required film thickness without failure while the deterioration of the characteristics is suppressed.

(Modifications)

In the present embodiment, as illustrated in FIG. 22, the side surface of the skirt-like insulation film 58 is inwardly convex. However, the side surface of the skirt-like insulation film 58 is not limited to the configuration illustrated in FIG. 22. FIGS. 24A and 24B are enlarged sectional views of the semiconductor device according to modifications of the present embodiment, which illustrate structures thereof.

For example, as illustrated in FIG. 24A, the side surface of the skirt-like insulation film 58 may be outwardly convex. In this case, the interface between the silicon oxide film 96 and the silicon nitride film 98 has a substantially outwardly convex part reflecting the configuration of the side surface of the skirt-like insulation film 58.

As illustrated in FIG. 24B, the side surface of the skirt-like insulation film 58 may be substantially plane. In this case, the interface between the silicon oxide film 96 and the silicon nitride film 98 has a substantially plane part reflecting the configuration of the side surface of the skirt-like insulation film 58.

In FIGS. 24A and 24B, the structures of the NMOS transistors 46 n are illustrated, but the PMOS transistor 46 p can have the same configuration of the side surface of the skirt-like insulation film 58 as illustrated in FIGS. 24A and 24B.

Modified Embodiments

The present invention is not limited to the above-described embodiments and can cover other various modifications.

For example, in the above-described embodiments, the CMOS transistor including the NMOS transistor 46 n and the PMOS transistor 46 p is explained. However, the present invention is applicable to the fabrication of an NMOS transistor alone or a PMOS transistor alone.

In the above-described embodiments, the gate electrodes 50 are formed of polysilicon film, but the material and the structure of the gate electrodes 50 are not limited to the above. For example, the gate electrodes 50 may have the polymetal structure of a layer of a metal film formed on a polysilicon film.

In the above-described embodiments, the skirt-like insulation film 58 is formed of silicon oxide film, but the material of the skirt-like insulation film 58 is not limited to silicon oxide film. For example, silicon oxide film forming the skirt-like insulation film 58 may contain carbon.

In the above-described embodiments, the sidewall insulation film 60 is formed of silicon oxynitride film and the layer film of the silicon oxide film 96 and the silicon nitride film 98. The material and the structure of the sidewall insulation film 60 are not limited to the above. For example, the silicon oxynitride film, silicon oxide film and silicon nitride film forming the sidewall insulation film 60 may contain carbon. The sidewall insulation film 60 can be a layer of 2 or more insulation films. For example, the sidewall insulation film 60 may be formed of the layer film of a silicon oxide film, a silicon nitride film and a silicon oxide film sequentially laid one on another. 

1. A semiconductor device comprising: a gate electrode formed over a semiconductor substrate with a gate insulation film formed therebetween; a source/drain diffused layer formed in the semiconductor substrate on both sides of the gate electrode; and a sidewall insulation film including a skirt-like first insulation film formed on a lower part of a side wall of the gate electrode, and a second insulation film formed on an exposed part of the side wall of the gate electrode, which is not covered by the first insulation film and on a side surface of the first insulation film.
 2. A semiconductor device according to claim 1, wherein the first insulation film covers an end of the source/drain diffused layer nearer to the gate electrode.
 3. A semiconductor device according to claim 1, wherein the source/drain diffused layer further comprises a first impurity diffused region forming an extension region of an extension source/drain structure, a second impurity diffused region whose end nearer to the gate electrode is positioned below the second insulation film and is deeper than the first impurity diffused region, and a third impurity diffused region whose end nearer to the gate electrode is extended to an end of the second insulation film and is deeper than the second impurity diffused region.
 4. A semiconductor device according to claim 2, wherein the source/drain diffused layer further comprises a first impurity diffused region forming an extension region of an extension source/drain structure, a second impurity diffused region whose end nearer to the gate electrode is positioned below the second insulation film and is deeper than the first impurity diffused region, and a third impurity diffused region whose end nearer to the gate electrode is extended to an end of the second insulation film and is deeper than the second impurity diffused region.
 5. A semiconductor device according to claim 1, wherein the first insulation film is formed of silicon oxide film.
 6. A semiconductor device according to claim 1, wherein the second insulation film is formed of silicon oxynitride film.
 7. A semiconductor device according to claim 1, wherein the second insulation film is a layer film of a third insulation film and a fourth insulation film sequentially laid the latter on the former.
 8. A semiconductor device according to claim 7, wherein the third insulation film is formed of silicon oxide film, and the fourth insulation film is formed of silicon nitride film.
 9. A semiconductor device according to claim 1, wherein the second insulation film is a layer film of a third insulation film, a fourth insulation film and a fifth insulation film sequentially laid one on another.